Avaliação do desgaste de porcelanatos esmaltados polidos

Assessment of wear of polished enameled porcelain tiles

Evaluación del desgaste del gres porcelánico esmaltado pulido

Isaura Morona Zaccaron, Laura Savi Rosso, Juliana de Oliveira Menegon, Aline Demarch, Angela Waterkemper Vieira, Pâmela Milak

Downloads: 6
Views: 800

Resumo

O Brasil destaca-se como o terceiro maior produtor global de revestimentos cerâmicos, ampliando a diversidade e qualidade desses materiais ao longo do tempo. A durabilidade comprovada faz das cerâmicas uma escolha popular para aplicações em pisos, paredes e fachadas, tanto em ambientes internos quanto externos. O porcelanato, conhecido por sua baixa absorção de água e alta resistência mecânica, tem crescido no mercado, especialmente com a introdução do porcelanato esmaltado polido, que apresenta efeitos decorativos e superfícies polidas. No entanto, desafios, como a abrasão superficial ao longo do tempo, têm levado os fabricantes a buscarem soluções para atender às demandas dos consumidores. Desta forma, este estudo tem como objetivo analisar a perda de brilho e massa na superfície do porcelanato esmaltado polido, buscando compreender a relação entre desgaste, quantificado pela perda de massa e brilho, e a percepção visual do material. Para isso, peças de porcelanato esmaltado polido produzidas industrialmente foram coletadas e submetidas aos testes. O desgaste superficial foi induzido por abrasão usando um abrasímetro Gabrielli, conforme ABNT NBR ISO 10545-7, com ciclos de 25 giros, progredindo até 4.000 giros. As amostras foram avaliadas visualmente e submetidas a medições de massa e brilho em Unidades de Brilho (UB). Os testes foram conduzidos em triplicata, com dados analisados pela média das medições. Equações matemáticas foram desenvolvidas para modelar o fenômeno. Os resultados indicam uma perda significativa de brilho nos produtos até 3.000 giros, destacando a sensibilidade desse atributo à abrasão superficial. Por outro lado, o teste de perda de massa, embora informativo, revela limitações de precisão devido à pequena quantidade de massa perdida em cada ciclo de abrasão, dificultando a quantificação precisa. A modelagem por meio de equações permitiu criar um modelo médio que representa a perda de brilho e massa para essa tipologia de produto. Essa abordagem pode ser estendida a outras tipologias, sujeitas a testes semelhantes, proporcionando uma ferramenta valiosa para compreender e prever o comportamento desses materiais diante da abrasão superficial.

Palavras-chave

Desgaste; abrasão superficial; porcelanato polido.

Abstract

Brazil stands out as the third largest world producer of ceramic tiles and the diversity and quality of these materials were expanded over time. Its durability makes ceramics a popular choice for floor, wall and facade applications, both indoors and outdoors. Porcelain tiles, known for their low water absorption and high strength, have grown on the market, especially with the introduction of polished enameled porcelain tiles, which have decorative effects and polished surfaces. However, problems as surface abrasion over time have led manufacturers to seek solutions to meet consumer demands. Therefore, this study aimed to analyze the loss of gloss and mass on the surface of polished enameled porcelain tiles in order to understand the relationship between wear, determined by the loss of mass and gloss, and the visual perception of the surfaces. For this, industrial polished enameled porcelain tiles were collected in the manufacturing line and tested. The surface wear was induced by abrasion using a Gabrielli abrasimeter, according to ABNT NBR ISO 10545-7 standard, in steps of 25 rotations until 4,000 rotations. The samples were visually inspected and subjected to mass (g) and brightness (BU) measurements. The tests were conducted in triplicate, analyzing the average and standard deviations. Regression equations were used to model the phenomenon. The results show a significant loss of gloss in the surfaces up to 3,000 rotations, highlighting the sensitivity of this factor to surface abrasion. On the other hand, the mass loss test, although informative, shows low precision due to the small amount of mass lost in each abrasion cycle, making precise quantification difficult. The regression equations showed an average model for the loss of gloss and mass for the product. This approach can be extended to other typologies, subject to similar tests, providing a valuable tool to understand and predict the behavior of these materials regarding surface abrasion.

Keywords

Wear; surface abrasion; polished porcelain.

Resumen

Brasil se destaca como el tercer productor mundial de baldosas cerámicas y la diversidad y calidad de estos materiales se fueron ampliando con el tiempo. Su durabilidad hace que la cerámica sea una opción popular para aplicaciones en pisos, paredes y fachadas, tanto en interiores como en exteriores. El gres porcelánico, conocido por su baja absorción de agua y alta resistencia, ha crecido en el mercado, especialmente con la introducción del gres porcelánico esmaltado pulido, que tiene efectos decorativos y superficies pulidas. Sin embargo, problemas como la abrasión de las superficies con el paso del tiempo han llevado a los fabricantes a buscar soluciones para satisfacer las demandas de los consumidores. Por tanto, este estudio tuvo como objetivo analizar la pérdida de brillo y masa en la superficie de gres porcelánico esmaltado pulido para comprender la relación entre el desgaste, determinado por la pérdida de masa y brillo, y la percepción visual de las superficies. Para ello, se recogieron en la línea de fabricación y se probaron piezas de gres porcelánico esmaltado pulido industrial. El desgaste superficial fue inducido por abrasión utilizando un abrasímetro Gabrielli, según norma ABNT NBR ISO 10545-7, en pasos de 25 rotaciones hasta 4.000 rotaciones. Las muestras fueron inspeccionadas visualmente y sometidas a mediciones de masa (g) y brillo (BU). Las pruebas se realizaron por triplicado, analizando la media y las desviaciones estándar. Se utilizaron ecuaciones de regresión para modelar el fenómeno. Los resultados muestran una pérdida significativa de brillo en las superficies hasta 3.000 rotaciones, destacando la sensibilidad de este factor a la abrasión superficial. Por otro lado, el ensayo de pérdida de masa, aunque informativo, muestra baja precisión debido a la pequeña cantidad de masa perdida en cada ciclo de abrasión, lo que dificulta una cuantificación precisa. Las ecuaciones de regresión mostraron un modelo promedio para la pérdida de brillo y masa del producto. Este enfoque puede extenderse a otras tipologías, sujetas a ensayos similares, proporcionando una valiosa herramienta para comprender y predecir el comportamiento de estos materiales respecto a la abrasión superficial.

Palabras clave

Desgaste; abrasión superficial; porcelana pulida.