Cerâmica Industrial
https://www.ceramicaindustrial.org.br/article/doi/10.4322/cerind.2024.043
Cerâmica Industrial
Regular Placas cerâmicas

Estudo de variáveis do ensaio de absorção de água em porcelanatos pelo método a vácuo

Study of the water absorption test on porcelain tiles using the vacuum method

Estudio del ensayo de absorción de agua en gres porcelánico mediante el método del vacío

Juliana de Oliveira Menegon, Laura Savi Rosso, Aline Demarch, Angela Waterkemper Vieira, Elidio Angioletto

Downloads: 1
Views: 125

Resumo

Os revestimentos cerâmicos desempenham um papel fundamental na construção civil, sendo amplamente utilizados, o que ressalta a importância de manter um controle rigoroso sobre suas propriedades físicas, com enfoque especial na porosidade e na capacidade de absorção de água. A absorção de água está ligada à porosidade residual e é influenciada pelo processo de sinterização e pela qualidade dos materiais cerâmicos. As normas de revestimentos cerâmicos classificam os produtos com base em seus níveis de absorção de água. O não cumprimento dessas normas pode resultar na perda do selo de qualidade ou na reclassificação do produto em uma categoria de absorção diferente, o que pode excluí-lo da categoria de porcelanatos. Portanto, justificam-se estudos para analisar o ensaio de absorção de água atualmente utilizado, que envolve a aplicação de vácuo, conforme a NBR ISO 10545-3 [1]. Este trabalho consistiu em avaliar a absorção de água das amostras, variando o tempo de imersão, o tempo do final da prova até a pesagem e a variação da pressão de vácuo no sistema. Foram utilizados cinco produtos classificados como porcelanatos esmaltados, fabricados em uma linha de produção industrial, com faixas de absorção de água pré-estabelecidas. Os resultados revelaram que as amostras não alcançaram a saturação em 15 minutos de imersão e que a absorção de água aumentou com o prolongamento do tempo de imersão. O tempo fora da água mostrou uma diminuição sutil na absorção de água à medida que o tempo avançava devido à evaporação da água dos poros do produto. Também se constatou que a variação da pressão de vácuo não teve um impacto significativo nos resultados de absorção de água das amostras testadas. Foi constatado que negligenciar o tempo de imersão pode levar à desclassificação do produto, destacando a importância de uma gestão adequada desse tempo para garantir a confiabilidade dos resultados.

Palavras-chave

Absorção de água; porosidade; pressão de vácuo; porcelanato; tempo de imersão.

Abstract

Ceramic tiles play a fundamental role in building industry, being widely used, which highlights the importance of maintaining strict control over their physical properties, with a special focus on porosity and water absorption capacity. Water absorption is linked to residual porosity and is influenced by the sintering process and the quality of ceramic materials. Ceramic tile standards classify products based on their water absorption levels. Failure to comply with these standards may result in the loss of the quality seal or the reclassification of the product into a different absorption category, which may exclude it from the porcelain tile category. Therefore, there is a need on studies on the water absorption test that currently uses the vacuum method, in accordance with NBR ISO 10545-3 standard. In this work, the water absorption test for porcelain tile samples was evaluated regarding the immersion time, the time from the end of the test to weighing and the variation of the vacuum pressure in the system. Five products classified as enameled porcelain tiles were used, manufactured on a production line, with pre-established water absorption ranges. The results showed that the samples did not reach saturation within 15 minutes of immersion and that water absorption increased with prolonged immersion time. The time out of the water showed a subtle decrease in water absorption as time progressed due to the evaporation of water from the product's pores. Varying the vacuum pressure did not have a significant impact on the water absorption results of the tested samples. Finally, neglecting the immersion time can lead to the disqualification of the product, highlighting the importance of properly managing this time to guarantee the reliability of the results.

Keywords

Water absorption; porosity; vacuum pressure; porcelain tiles; immersion time.

Resumen

Las baldosas cerámicas desempeñan un papel fundamental en la industria de la construcción, siendo ampliamente utilizadas, lo que pone de relieve la importancia de mantener un estricto control sobre sus propiedades físicas, con especial atención a la porosidad y la capacidad de absorción de agua. La absorción de agua está ligada a la porosidad residual y está influenciada por el proceso de sinterización y la calidad de los materiales cerámicos. Las normas sobre baldosas cerámicas clasifican los productos según sus niveles de absorción de agua. El incumplimiento de estas normas puede conllevar la pérdida del sello de calidad o la reclasificación del producto en una categoría de absorción diferente, lo que podrá excluirlo de la categoría de gres porcelánico. Por lo tanto, es necesario realizar estudios sobre la prueba de absorción de agua que actualmente utiliza el método de vacío, de acuerdo con la norma NBR ISO 10545-3. En este trabajo se evaluó la prueba de absorción de agua para muestras de gres porcelánico en cuanto al tiempo de inmersión, el tiempo desde el final de la prueba hasta el pesaje y la variación de la presión de vacío en el sistema. Se utilizaron cinco productos clasificados como gres porcelánico esmaltado, fabricados en línea de producción, con rangos de absorción de agua preestablecidos. Los resultados mostraron que las muestras no alcanzaron la saturación dentro de los 15 minutos posteriores a la inmersión y que la absorción de agua aumentó con el tiempo de inmersión prolongado. El tiempo fuera del agua mostró una sutil disminución en la absorción de agua a medida que avanzaba el tiempo debido a la evaporación del agua de los poros del producto. La variación de la presión de vacío no tuvo un impacto significativo en los resultados de absorción de agua de las muestras analizadas. Finalmente, descuidar el tiempo de inmersión puede conllevar la descalificación del producto, resaltando la importancia de gestionar adecuadamente este tiempo para garantizar la confiabilidad de los resultados.

Palabras clave

Absorción de agua; porosidad; presión de vacío; gres porcelánico; tiempo de inmersión.