Caracterização mineralógica, físico-química e tecnológica da argila de Angélica (Brasil): Adequação para aplicação em produtos de construção

Mineralogical, physical-chemical and technological characterization of Angélica clay (Brazil): Suitability for application in construction products

Caracterización mineralógica, físico-química y tecnológica de la arcilla de Angélica (Brasil): Idoneidad para su aplicación en productos de construcción

Rafael Henrique de Oliveira; Cícero Rafael Cena da Silva; Daniel Araújo; Diogo Duarte dos Reis

Downloads: 7
Views: 654

Resumo

Neste trabalho, a argila localizada no município de Angélica, região centro oeste do Brasil, foi coletada e investigada quanto às suas características físicas, químicas, mineralógicas e de queima para avaliar sua potencial adequação em diversas aplicações cerâmicas. As propriedades químicas, mineralógicas e térmicas foram avaliadas pelas técnicas FRX e XRD e TGA, respectivamente. As características de queima foram medidas por cor, perda de massa, absorção de água, retração linear de secagem e de queima e resistência à flexão a partir de corpos de prova prensados e sinterizados a 800, 900, 1000, 1100 e 1200 °C. As morfologias da fratura dos corpos de prova foram verificadas por SEM. Os resultados mostram que essa matéria-prima possui predominância de quartzo, caulinita e muscovita e baixo teor de óxidos fundentes, o que resultou em sua característica refratária até 1100 °C. O teor relativamente baixo de Fe2O3 foi o responsável pelas cores claras na queima. À luz dos resultados deste estudo, nota-se que essa matéria-prima é promissora para fabricação de cerâmicas de cor clara estruturais, assim como para aplicações em revestimentos internos de parede, tijolos aparentes e telhas os quais apresentam maior valor agregado que tijolos e blocos de vedação estruturais produzidos atualmente na região.

Palavras-chave

Argila; Propriedades tecnológicas; Indústria cerâmica.

Abstract

In this work, one clay from the county of Angélica, central western region of Brazil, was collected and investigated regarding its physical, chemical, mineralogical and firing characteristics to evaluate its suitability for ceramic processing. The chemical, mineralogical and thermal properties were evaluated by XRF and XRD and TGA techniques, respectively. The firing characteristics were measured by color differences, mass loss, water absorption, drying and firing linear shrinkage and flexural strength from specimens pressed and sintered at 800, 900, 1000, 1100 and 1200 °C. The fracture morphologies of the specimens were analyzed by SEM. The results show that this raw material has a predominance of quartz, kaolinite and muscovite and low content of fluxing oxides, which resulted in its refractory characteristic up to 1100 °C. The relatively low content of Fe2O3 was responsible for the light colors on firing. In light of the results of this study, it is noted that this raw material is promising for the manufacture of light-colored structural ceramics, as well as for applications in internal wall coverings, exposed bricks and tiles, which show greater added value than bricks and blocks currently produced in the region.

Keywords

Clay; Technological properties; Ceramic industry.

Resumen

En este trabajo, una arcilla del municipio de Angélica, región centro-oeste de Brasil, fue recolectada e investigada en cuanto a sus características físicas, químicas, mineralógicas y de cocción para evaluar su idoneidad para el procesamiento cerámico. Las propiedades químicas, mineralógicas y térmicas se evaluaron mediante técnicas XRF y XRD y TGA, respectivamente. Las características de cocción se midieron por diferencias de color, pérdida de masa, absorción de agua, contracción lineal por secado y cocción y resistencia a la flexión de especímenes prensados ​​y sinterizados a 800, 900, 1000, 1100 y 1200 °C. Las morfologías de fractura de los especímenes fueron analizadas por SEM. Los resultados muestran que esta materia prima tiene predominio de cuarzo, caolinita y moscovita y bajo contenido de óxidos fundentes, lo que le confiere su característica refractaria hasta los 1100 °C. El contenido relativamente bajo de Fe2O3 fue el responsable de los colores claros al cocer. A la luz de los resultados de este estudio, se percibe que esta materia prima es promisoria para la fabricación de cerámicas estructurales de colores claros, así como para aplicaciones en revestimientos de paredes internas, ladrillos cara vista y tejas, que presentan mayor valor agregado que los ladrillos y bloques actualmente producidos en la región.

Palabras clave

Arcilla; Propiedades tecnológicas; Industria cerámica.